| Properties | Test method | Test condition | Unit | CEVIAN ABS |
| V-2 Standard | ||||
| AF800 | ||||
| Melt mass-flow rate | ISO 1133 |
200℃/5kg |
g/10min |
7 |
| Mold shrinkage |
ASTM D955 | % |
0.4 - 0.6 | |
| Tensile strength |
ISO 527 |
MPa | 50 | |
| Flexural strength |
ISO178 |
MPa | 74 | |
| Flexural modulus |
ISO178 |
MPa | 2700 | |
| Charpy notched
impact strength |
ISO 179/1eA |
23℃ | kJ/m2 | 10 |
| Izod notched
Impact strength |
ASTM D256 |
23℃ /6.4mm | J/m | - |
| Rockwell hardness |
ISO 2039 |
- | - | |
| Deflection temperature
under load |
ISO 75 ASTM D648 |
1.80MPa 1.82MPa/12.7mm |
℃ | 70 - |
| Vicat softening
temperature |
ISO 306/B50 | 50N,50℃/h | ℃ | - |
| Coefficient of
thermal expansion |
ISO 11359 | ×10-5/℃ | 9 | |
| Flamability * |
UL94 |
- | V-2/0.75mｍ | |
| Dielectric strength |
ASTM D149 |
1.5mm | MV/m | - |
| Arc resistance * |
ASTM D495 |
3.0mm | sec (PLC) |
- |
| Water absorption |
ISO 62 |
% |
0.3 | |
| Density |
ISO 1183 |
g/cm3 |
1.08 |
NOTES