[Materials data sheet] CEVIAN V　AS resin

Properties Test method Test condition Unit General purpose Easy flow Heat resistant Transparent UV resistant For Plating For Extrusion Chemical resistant Sliding GF-reinforced
GF10% GF20% GF30%
300
300SF		 320
320SF 		500
500SF 		510
510SF 		520
520SF 		660
660SF 		680
680SF 		400N 400NF 400T
400TF 		466MD 464MD 462M 460M 450SF T500 T500SF T550 T550SF T800 T800SF 650 MX5 720 860 910B VGR10 VGR10F VGR20 VGR20F VGR30 VGR30F
Melt mass-flow rate ISO 1133 220℃/10kg g/10min 12 17 19 21 22 45 55 2 3.5 4 7 15 20 10 25 28 27 20 12 6 13 22 - - -
Mold shrinkage ASTM D955 　 % 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.7 0.4 - 0.6 0.5 - 0.8 0.5 - 0.6 0.4 - 0.7 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 - 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.2 - 0.5 0.1 - 0.4 0.1 - 0.4
Tensile strength ISO 527 　 MPa 37 43 48 51 55 47 42 50 42 43 43 43 43 51 42 48 41 48 49 41 46 46 80 90 100
Flexural strength ISO178 　 MPa 60 70 75 80 95 75 70 72 66 69 69 67 67 80 63 74 55 75 67 60 68 68 110 130 150
Flexural modulus ISO178 　 MPa 1900 2300 2500 2700 3000 2500 2300 2400 2300 2300 2300 2400 2400 2600 2000 2300 2000 2500 2300 2100 2500 2600 4800 6800 8800
Charpy notched impact strength ISO 179/1eA 23℃
-30℃ 		kJ/m2 40
25 		30
17 		20
10 		10
6 		5
3 		20
8 		25
10 		12
5 		11
7 		10
- 		12
- 		16
- 		21
- 		18
12 		14
- 		9
-		 10
- 		18
9 		24
- 		25
14 		30
- 		10
- 		10
6 		10
7 		10
8
Izod notched Impact strength ASTM D256 23℃/6.4mm
-30℃/6.4mm		 J/m 400
280 		300
150 		200
100 		100
60 		50
30 		200
120 		250
130 		120
40 		110
70 		100
- 		120
- 		160
- 		210
- 		180
120 		-
- 		-
-		 -
- 		200
90 		-
- 		250
140 		-
- 		100
- 		120
40 		110
40
100
40
Rockwell hardness ISO 2039 　 - R90 R110 R110 R110 R115 R110 R110 R102 R112 - - R110 R110 R115 - - - R115 - R110 - - R115 R115 R117
Deflection temperature under load ISO 75
ASTM D648 		1.80MPa
1.82MPa/12.7mm 		℃ 74
84 		77
87 		78
89 		80
91 		81
92 		77
87 		76
86 		101
115 		96
111 		101
- 		95
- 		90
- 		85
- 		81
94 		68
- 		73
-		 67
- 		80
91 		82
- 		77
92 		81
94 		79
90 		96
104 		98
106 		100
108
Vicat softening temperature ISO 306/B50 50N,50℃/h ℃ 89
 93 95 98 98 94 92 - 106 - - - - 100 - - - - - 96 - - 99 103 104
Ball pressure registration temperature - 　 ℃ 90 90 90 90 - 90 90 120 - - - 100 - - - - 　- 90 - 90 - - 95 95 95
Coefficient of thermal expansion ISO 11359 MD
TD		 ×10-5/℃ 9
- 		8
- 		8
- 		8
- 		8
- 		8
- 		8
- 		6
- 		8
- 		8
- 		8
- 		8
- 		8
- 		8
- 		-
- 		-
-		 -
- 		-
- 		-
- 		9
- 		-
- 		8
- 		5
8 		4
8 		3
8
Flamability * UL94 　 - HB1.5-3.0mm HB1.5-3.0mm HB HB HB HB HB HB HB
1.5-2.9mm 		- - HB - HB HB HB - - - - - HB HB HB HB
Dielectric strength ASTM D149 1.5mm MV/m - - 32 36 - - - - - - - - - - - - - - - - - 26 - - -
Arc resistance * ASTM D495 3.0mm sec
(PLC)		 - - 102
(6) 		91
(6) 		- - - - - - - - - - - - - - - - - 81
(6) 		- - -
Light transmission ASTM D1003 　 % - - - - - - - - - - - - - - 89 90 89 - - - - - - - -
Water absorption ISO 62 　　 % 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 - - - - 0.3 - 0.3 - 0.3 0.3 0.3 0.3
Density ISO 1183 　　 g/cm3 1.03 1.05 1.05 1.06 1.06 1.05 1.05 1.05 1.05 1.07 1.07 1.06 1.05 1.05 1.09 1.11 1.08 1.05 1.04 1.05 1.05 1.04 1.11 1.19 1.27

NOTES
1. UL recognition File No. of Daicel Polymer is E47773.
2. Values with asterisk (*) are UL-recognized values.
3. CF-reinforced grades come under Item 5 (18) of Annex 1 of the Export Trade Control Order on the basis of the Foreign Exchange and Foreign Trade Law of Japan.