[Materials data sheet] NOVALLY A　PA/ABS

Properties Test method Test condition Unit General purpose GF-reinforced Flame retardant CF-reinforced
GF10% GF20% GF30% GF30% GF40% GF20% GF20% CF5% CF30% Flame retardant
A1300/A1300F A1500 A1700 A2602 A2604 A2606 A2506 A2706 A2508
（Type V）		 A5624 A5734 AC2601
（Type M）		 EAG423 AC5402
（Type P）
Dry Water content1.6% Dry Water content2.0% Dry Water content2.7% Dry Water content1.5% Dry Water content1.1% Dry Water content0.7% Dry Water content0.7% Dry Water content1.1% Dry Water content0.5% Dry Water content1.0% Dry Water content1.0% Dry Dry Dry
Mold shrinkage ASTM D955   % 0.4 - 0.6 - 0.6 - 0.8 - 0.8 - 1.1 - 0.3 - 0.6 - 0.2 - 0.5 - 0.1 - 0.5 - 0.1 - 0.5 - 0.1 - 0.5 - 0.1 - 0.4 - 0.2 - 0.5 - 0.2 - 0.5 - 0.3 - 0.6 0.1 - 0.5 0.1 - 0.2
Tensile strength ISO 527 　 MPa 42 36 42 33 50 33 69 51 94 71 120 95 110 88 120 93 137 114 96 77 106 86 86 185 100
Flexural strength ISO178 　 MPa 65 53 62 44 74 42 113 83 150 115 170 135 180 146 190 150 220 193 161 130 171 136 130 300 130
Flexural modulus ISO178 　 MPa 2000 1600 1800 1200 2200 960 3400 2300 5300 3600 6800 5500 7200 6000 7400 5100 10000 9000 6300 5100 6400 4800 4400 19000 8000
Charpy notched impact strength ISO179/1eA 23℃
-30℃		 kJ/m2 57
15		 60
-		 83
16		 78
-		 16
7		 40
-		 13
-		 14
-		 15
10		 16
-		 16
11		 18
-		 15
10 		16
- 		14
9 		16
- 		15
- 		17
- 		12
- 		13
- 		11
- 		12
- 		-
-		 10
-		 6
-
Izod notched Impact strength ASTM D256 23℃/6.4mm
-30℃/6.4mm 		J/m 570
150		 660
-		 830
160		 850
-		 160
70		 440
-		 120
-		 130
-		 150
100		 180
-		 160
110		 190
-		 150
100 		180
- 		140
90 		160
- 		150
- 		170
- 		120
- 		-
- 		110
- 		-
- 		74
-		 -
-		 -
-
Rockwell hardness ISO 2039 　 - R112 R105 R108 R101 R116 R109 R115 R114 R116 R115 R116 R115 R116 R115 R117 R115 R118 R117 R116 R115 R116 R115 - - -
Deflection temperature under load ISO 75
ASTM D648
ISO 75
ASTM D648 		1.80MPa
1.82MPa/6.4mm
0.45MPa
0.46MPa/6.4mm
℃
℃
℃
℃ 		80
90
97
97		 70
84
90
93		 74
84
100
100		 70
80
90
92		 70
80
105
105		 70
78
95
99		 100
110
205
205		 92
102
200
200		 170
180
210
210		 155
165
205
205		 185
195
215
215		 170
180
210
210		 160
160
205
205		 150
140
200
190		 190
200
220
220		 180
195
210
215		 185
185
213
213		 175
178
210
210		 181
183
212
213		 176

 210 

 194
198
216
217		 190

 214 
 -
120
-
200		 200
-
-
-		 120
-
170
-
Ball pressure registration temperature -   ℃ - - - - - - - - - - - - - - - - 180 - - - - - - - -
Coefficient of thermal expansion ISO11359 MD
TD		 ×10-5/℃ 10
- 		-
- 		10
- 		-
- 		10
- 		-
- 		6
10 		-
- 		5
10 		-
- 		3
10 		-
- 		2
10 		-
- 		3
10 		-
- 		2
10 		-
- 		5
10 		-
- 		5
10 		-
- 		-
- 		-
-		 -
-
Flamability * UL94 　 - HB - HB - HB - HB - HB - HB - HB - HB - HB - V-0/
0.75mm		 - V-0/
1.5mm		 - - - V-0/
0.75mm
Dielectric strength ASTM D149 1.5mm MV/m - -　 - - - - 14 - 14 - 14 - - 　  15 　  - 　  - 　  - 　  - - -
Arc resistance * ASTM D495 3.0mm sec
(PLC)
 - - - - - - 92
(6) 		- 92
(6) 		- 92
(6) 		- -   94
(6) 		  -   -   -   - - -
Water absorption ISO 62 　　 % 0.5 - 0.7 - 1.0 - 0.7 - 0.7 - 0.6 - 0.5 - 0.7 - 0.5 - 0.6 - 0.6 - - - -
Density ISO 1183 　　 g/cm3 1.05 - 1.06 - 1.09 - 1.14 - 1.23 - 1.30 - 1.28 - 1.31 - 1.38 - 1.45 - 1.46 - 1.1 1.24 1.34
Volume Resistivity ASTM D257   Ω・ｍ                                             102-105 100 101-103
Surface Resistivity ASTM D257   Ω                                                 103-106

NOTES
1. UL recognition File No. of Daicel Polymer is E47773.
2. Values with asterisk (*) are UL-recognized values.
3. CF-reinforced grades come under Item 5 (18) of Annex 1 of the Export Trade Control Order on the basis of the Foreign Exchange and Foreign Trade Law of Japan.