| Properties | Test method | Test condition | Unit | General purpose | GF-reinforced | Flame retardant | Enhanced surface appearance grades (PBT/ABS) | Enhanced surface appearance grades (PBT/PET) |
|||||||||||||||||
| Standard | Impact resistant | Standard | Heat resistant | Heat resistant | Low warpage | Standard | Heat resistant | Heat resistant/ Easy flow |
Low warpage | Heat resistant・ Low warpage |
General purpose | Flame retardant | General purpose | ||||||||||||
| - | - | - | - | GF20% | GF30% | GF15% | GF30% | Filler40% | - | GF20% | GF30% | GF30% | GF15% | GF30% | GF30% | GF30% | Filler40% | Filler30% | GF15% | GF15% | GF18% | ||||
| B1300 B1300F |
B1500 B1500F |
B1700 B1700F |
B14M0 | B2504 | B2506 | B2703 | B2706 | B3708 (Type K) |
B45M0 | B5524 | B5526 | B5546 (Type D) |
B5723 | B5726 | B5746 (Type D) |
B5746 (Type J) |
B6528 | B6726 | B27B3 （Type M1） |
B50B3 | BE2703 （Type K） |
||||
| Mold shrinkage | ASTM D955 | % | 0.5 - 0.8 | 0.7 - 0.9 | 1.2 - 1.4 | 0.6 - 0.9 | 0.3 - 0.5 | 0.2 - 0.4 | 0.4 - 0.7 | 0.3 - 0.6 | 0.2 - 0.4 | 0.6 - 0.8 | 0.25 - 0.45 | 0.2 - 0.4 | 0.2 - 0.4 | 0.4 - 0.6 | 0.3 - 0.5 | 0.3 - 0.5 | 0.3 - 0.5 | 0.2 - 0.3 | 0.2 - 0.4 | 0.4 - 0.6 | 0.4 - 0.6 | 0.2 - 0.4 | |
| Tensile strength | ISO 527 | MPa | 38 | 42 | 47 | 40 | 86 | 103 | 81 | 115 | 100 | 44 | 95 | 110 | 110 | 91 | 120 | 115 | 120 | 95 | 93 | 80 | 80 | 100 | |
| Flexural strength | ISO178 | MPa | 57 | 67 | 74 | 60 | 140 | 150 | 130 | 170 | 160 | 70 | 135 | 160 | 170 | 130 | 185 | 185 | 180 | 150 | 155 | 115 | 125 | 150 | |
| Flexural modulus | ISO178 | MPa | 1800 | 2200 | 2400 | 1900 | 6000 | 8400 | 5200 | 8900 | 11500 | 2500 | 6600 | 9200 | 9500 | 5600 | 9700 | 9700 | 9700 | 11000 | 9700 | 5000 | 5000 | 6000 | |
| Charpy notched impact strength | ISO179/1eA | 23℃ | kJ/m2 | 10 | 3 | 3 | 50 | 8 | 9 | 6 | 8 | 7 | 3 | 7 | 8 | 8 | 6 | 8 | 6 | 8 | 7 | 6 | 6 | 4 | 5 |
| Izod notched Impact strength | ASTM D256 |
23℃ /6.4mm | J/m | 60 | 30 | 30 | - | 80 | 90 | 60 | 80 | 60 | 30 | 70 | 80 | 80 | 60 | 80 | 60 | 70 | 70 | 60 | - | - | - |
| Deflection temperature under load | ISO 75 ASTM D648 ISO 75 ASTM D648 |
1.80MPa 1.82MPa/6.4mm 0.45MPa 0.46MPa/6.4mm |
℃ | 80 90 100 100 |
80 90 100 100 |
75 85 150 150 |
80 - - - |
130
125 200 200 |
140 150 205 205 |
160 185 205 205 |
190 200 210 210 |
190 200 210 210 |
85 100 115 115 |
130 125 200 200 |
140 155 210 210 |
145 150 210 210 |
175 185 210 210 |
190 200 220 220 |
190 200 220 220 |
190 200 220 220 |
140 155 205 205 |
185 195 215 215 |
155 180 200 200 |
160 - 210 - |
180 - - - |
| Ball pressure registration temperature | - | ℃ | - | 105 |
- | - | - | - | 180 | - | - | - | - | 160 | - | 190 | 200 | - | - | - | - | 190 | - | - | |
| Coefficient of thermal expansion | ISO 11359 | MD TD |
×10-5/℃ | 10 - |
10 - |
10
- |
10 - |
3 10 |
2 10 |
3 10 |
2 10 |
3 8 |
10 - |
3 10 |
2 10 |
2 10 |
3 10 |
2 10 |
2 10 |
2 10 |
3 8 |
3 8 |
3 10 |
- | - |
| Flamability * | UL94 | - | - | HB | HB | - | HB | HB | HB | HB | HB | V-0/ 1.2mm | V-0/1.5mm 5VA/2.9mm |
V-0/ 1.5mm | V-0/ 1.5mm | V-0/1.5mm | V-0/1.5mm 5VA/2.0mm |
V0/1.5mm 5VA/2.0mm |
V-0/1.5mm 5VA/2.0mm |
V-0/1.6mm | V-0/1.5mm | HB | V-0/1.5mm | - | |
| Dielectric strength | ASTM D149 | 1.5mm | MV/m | - | 31 | 28 | - | 35 | 35 | 35 | 35 | 24 | 31 | 30 | 30 | 27 | 29 | 29 | 26 | 26 | 27 | 26 | - | - | - |
| Arc resistance * | ASTM D495 | 3.0mm | sec (PLC) |
- - |
101 (6) |
128 (5) |
- - |
85
(6) |
85 (6) |
- - |
- - |
124 (5) |
79 (6) |
69
(6) |
69 (6) |
-
(6) |
-
(6) |
- (6) |
72 (6) |
72 (6) |
69 (6) |
77 (6) |
- | - | - |
| Hot wire ignition * | UL746A | 1.5mm | sec (PLC) |
- - |
13 (4) |
10 (4) |
- - |
50 (2) |
50 (2) |
13 (4) |
13 (4) |
13
(4) |
18
(3) |
24 (3) |
24 (3) |
31 (2) |
27 (3) |
27 (3) |
25 (3) |
25 (3) |
22 (3) |
22 (3) |
- | - | - |
| High ampere arc ignition * | UL746A | 1.5mm | (PLC) | - - |
150 (0) |
150 (0) |
- - |
113 (1) |
113 (1) |
68 (1) |
68 (1) |
19 (3) |
150 (0) |
35 (2) |
35 (2) |
19 (3) |
25 (3) |
25 (3) |
33 (2) |
33 (2) |
39 (2) |
75 (1) |
- | - | - |
| High voltage tracking rate * | UL746A | 3.0mm | mm/min (PLC) |
- - |
17 (1) |
19 (1) |
- - |
25 (1) |
25 (1) |
1.2
(0) |
1.2 (0) |
15 (1) |
5 (0) |
187 (4) |
187 (4) |
208 (4) |
87 (3) |
87 (3) |
150 (4) |
150 (4) |
288 (4) |
65 (2) |
- | - | - |
| Comparative tracking Index * | IEC 112 | 3.0mm | V
(PLC) |
- - |
600 (0) |
600 (0) |
- - |
600 (0) |
600 (0) |
500 (1) |
500 (1) |
430 (1) |
400 (1) |
210 (3) |
210 (3) |
- (3) |
225 (3) |
225 (3) |
220 (3) |
220 (3) |
200 (3) |
240 (3) |
- | - | - |
| Water absorption | ISO 62 | % | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | 0.15 | - | - | |
| Density | ISO 1183 | g/cm3 | 1.12 | 1.17 | 1.23 | 1.13 | 1.31 | 1.39 | 1.33 | 1.44 | 1.56 | 1.32 | 1.42 | 1.50 | 1.50 | 1.43 | 1.55 | 1.55 | 1.54 | 1.61 | 1.56 | 1.33 | 1.46 | 1.45 | |
NOTES
1. UL recognition File No. of Daicel Polymer is E47773.
2. Values with asterisk (*) are UL-recognized values.
3. CF-reinforced grades come under Item 5 (18) of Annex 1 of the Export Trade Control Order on the basis of the Foreign Exchange and Foreign Trade Law of Japan.