| Properties | Test method | Test condition | Unit | General purpose | Flame retardant | |
| Standard | UV resistant / Impact resistant | Impact resistant | ||||
| CE1810 | CE1820 | CB4830 | ||||
| Mold shrinkage | ASTM D955 | % | 0.5 - 0.7 | 0.5 - 0.7 | 0.4 - 0.6 | |
| Tensile strength | ISO 527 | MPa | 63 | 58 | 62 | |
| Flexural strength | ISO178 | MPa | 90 | 80 | 90 | |
| Flexural modulus | ISO178 | MPa | 2300 | 2200 | 2300 | |
| Charpy notched impact strength | ISO179/1eA | 23℃ | kJ/m2 | 20 | 60 | 45 |
| Deflection temperature under load | ISO 75 | 1.80MPa 0.45MPa |
℃ | 115 135 |
112 130 |
95 - |
| Flamability | UL94 | - | - | - | V-0/0.75mm | |
| Hot wire ignition | UL746A | 3.0mm | (PLC) | - | - | (2) |
| High ampere arc ignition | UL746A | 0.75mm 3.0mm |
(PLC) (PLC) |
- - |
- - |
(3) (0) |
| Comparative tracking Index | IEC112 | 3.0mm | (PLC) | - | - | (2) |
| Density | ISO 1183 | g/cm3 | 1.22 | 1.21 | 1.31 | |
NOTES
1. UL recognition File No. of Daicel Polymer is E47773.
2. Values with asterisk (*) are UL-recognized values.
3. CF-reinforced grades come under Item 5 (18) of Annex 1 of the Export Trade Control Order on the basis of the Foreign Exchange and Foreign Trade Law of Japan.