| Properties | Test method | Test condition | Unit | NOVALLOY X PC/HIP | NOVALLOY S PC/ABS | |||||||
| V-0 Standard | V-1 Easy flow | V-0 Easy flow | V-0 Standard | V-0 Heat resistant | V-0 Easy flow | V-0 Easy flow | V-0 High-Heat resistant | V-1Filled, | ||||
| X7203L （Type V） |
X7303L | X72S2 | S6500L | S6700 | S6900 | S7600 | S7900 （Type G） |
S66S4 | ||||
| Melt mass-flow rate | ISO 1133 | 220℃/10kg 240℃/5kg |
g/10min | 40 - |
50 - |
50 - |
45 26 |
31 21 |
- 11 |
- 40 |
- 13 |
- - |
| Mold shrinkage | ASTM D955 | % | 0.4 - 0.6 | 0.4 - 0.6 | 0.4 - 0.6 | 0.4 - 0.6 | 0.4 - 0.6 | 0.4 - 0.6 | 0.4 - 0.6 | 0.4 - 0.6 | 0.2-0.3 | |
| Tensile strength | ISO 527 | MPa | 53 | 48 | 48 | 54 | 61 | 64 | 60 | 65 | 75 | |
| Flexural strength | ISO178 | MPa | 84 | 79 | 85 | 85 | 96 | 93 | 94 | 94 | 125 | |
| Flexural modulus | ISO178 | MPa | 2600 | 2600 | 2600 | 2600 | 2800 | 2640 | 2700 | 2740 | 6200 | |
| Charpy notched impact strength | ISO 179/1eA | 23℃ | kJ/m2 | 20 | 41 | 14 | 15 | 10 | 10 | 9 | 10 | 7 |
| Izod notched Impact strength | ASTM D256 | 23℃/6.4mm | J/m | 390 | 290 | - | 200 | 150 | - | - | - | - |
| Rockwell hardness | ISO 2039 | - | - | - | - | - | - | - | - | - | - | |
| Deflection temperature under load | ISO 75 ASTM D648 |
1.80MPa 1.82MPa/12.7mm |
℃ | 81 92 |
79 87 |
80 - |
79 85 |
86 95 |
102 - |
80 - |
96 - |
94 - |
| Vicat softening temperature | ISO 306/B50 ASTM D1525 |
50N,50℃/h 9.8N,50℃/h |
℃ | 97 - |
93 - |
- - |
94 - |
101 - |
- - |
- - |
- - |
- - |
| Ball pressure registration temperature | - | ℃ | - | - | - | - | 90 | - | - | - | - | |
| Coefficient of thermal expansion | ISO 11359 | ×10-5/℃ | 7 | 7 | 7 | - | - | - | - | - | MD/4 TD/5 |
|
| Flamability * | UL94 | - | V-0/1.5mm 5VB/2.0mm 5VA/2.5mm |
V-1/1.8mm V-0/2.5mm 5VA/2.5mm |
V-0/1.5mm 5VB/2.0mm 5VA/2.5mm |
V-0/1.6mm 5VA/2.5mm |
V-0/1.6mm 5VB/2.0mm 5VA/2.5mm |
V-0/1.5mm | V-0/1.2mm 5VB/2.0mm 5VA/2.5mm |
V-2/0.75mm V-0/1.0mm 5VB/2.0mm |
V-2/0.75mm (blk) V-1/1.5mm (blk) V-2/0.75mm (blk) |
|
| Dielectric strength | ASTM D149 | 1.5mm | MV/m | - | - | - | 23 | 21 | - | - | - | - |
| Arc resistance * | ASTM D495 | 3.0mm | sec (PLC) |
- | - | - | 106 (6) |
118 (6) |
- | - | - | - |
| Water absorption | ISO 62 | % | 0.3 | 0.3 | 0.3 | 0.3 | 0.3 | - | 0.3 | - | - | |
| Density | ISO 1183 | g/cm3 | 1.17 | 1.16 | 1.17 | 1.17 | 1.17 | 1.20 | 1.18 | 1.19 | 132 | |
NOTES
1. UL recognition File No. of Daicel Polymer is E47773.
2. Values with asterisk (*) are UL-recognized values.
3. CF-reinforced grades come under Item 5 (18) of Annex 1 of the Export Trade Control Order on the basis of the Foreign Exchange and Foreign Trade Law of Japan.