[Materials data sheet]
Novalloy A / PA/ABS

Properties
Test method
Test condition
Unit
General purpose
GF-reinforced
Flame retardant
 CF-reinforced
GF10%
GF20%
GF30%
 GF30% GF40% GF20% GF20% CF5% CF30%
A1300/A1300F
A1500
A1700
A2602
A2604
A2606
 A2506 A2706 A2508
(Type V)		 A5624 A5734 AC2601M EAG423
Dry
Water content
1.6%
Dry
Water content
2.0%
Dry
Water content
2.7%
Dry
Water content
1.5%
Dry
Water content
1.1%
Dry
Water content
0.7%
 Dry Water content
0.7%		 Dry Water content
1.1%		 Dry Water content
0.5%		 Dry Water content
1.0%		 Dry Water content
1.0%		 Dry  
Mold shrinkage
ASTM D955
 
%
0.4-0.6
-
0.6-0.8
-
0.8-1.1
-
0.3-0.6
-
0.2-0.5
-
0.1-0.5
-
 0.1-0.5 - 0.1-0.5 - 0.1-0.4 - 0.2-0.5 - 0.2-0.5 - 0.3-0.6 0.1-0.5
Tensile strength
ISO 527
 
MPa
42
36
42
33
50
33
69
51
94
71
120
95
 110 88 120 93 137 114 96 77 106 86 86 185
Flexural strength
ISO178
 
MPa
65
53
62
44
74
42
113
83
150
115
170
135
 180 146 190 150 220 193 161 130 171 136 130 300
Flexural modulus
ISO178
 
MPa
2000
1600
1800
1200
2200
960
3400
2300
5300
3600
6800
5500
 7200 6000 7400 5100 10000 9000 6300 5100 6400 4800 4400 19000
Charpy notched impact strength
ISO179/1eA
23℃
-30℃
kJ/m2
57
15
60
-
83
16
78
-
16
7
40
-
13
-
14
-
15
10
16
-
16
11
18
-
 15
10 		16
- 		14
9 		16
- 		15
- 		17
- 		12
- 		13
- 		11
- 		12
- 		-
-		 10
-
Izod notched Impact strength
ASTM D256
23℃ /6.4mm
-30℃/6.4mm
J/m
570
150
660
-
830
160
850
-
160
70
440
-
120
-
130
-
150
100
180
-
160
110
190
-
 150
100 		180
- 		140
90 		160
- 		150
- 		170
- 		120
- 		-
- 		110
- 		-
- 		74
-		 -
-
Rockwell hardness
ISO 2039
 
-
R112
R105
R108
R101
R116
R109
R115
R114
R116
R115
R116
R115
 R116 R115 R117 R115 R118 R117 R116 R115 R116 R115 - -
Deflection temperature under load
ISO 75
ASTM D648
ISO 75
ASTM D648
1.80MPa
1.82MPa/6.4mm
0.45MPa
0.46MPa/6.4mm
℃
℃
℃
℃
80
90
97
97
70
84
90
93
74
84
100
100
70
80
90
92
70
80
105
105
70
78
95
99
100
110
205
205
92
102
200
200
170
180
210
210
155
165
205
205
185
195
215
215
170
180
210
210
 160
160
205
205		 150
140
200
190		 190
200
220
220		 180
195
210
215		 185
185
213
213		 175
178
210
210		 181
183
212
213		 176

 210 

 194
198
216
217		 190

 214 
 -
120
-
200		 200
-
-
-
Coefficient of thermal expansion
ISO11359
MD
TD
×10-5/℃
10
-
-
-
10
-
-
-
10
-
-
-
6
10
-
-
5
10
-
-
3
10
-
-
2
10
-
-
3
10
-
-
2
10
-
-
5
10
-
-
5
10
-
- 		-
- 		-
-
Flamability *
UL94
 
-
HB
-
HB
-
HB
-
HB
-
HB
-
HB
-
HB
-
HB
-
HB
-
V-0/
0.75mm
-
V-0/
1.5mm
 - - -
Dielectric strength
ASTM D149
1.5mm
MV/m
-
-
-
-
-
-
14
-
14
-
14
-
-
 
15
 
-
 
-
 
-
   - -
Arc resistance *
ASTM D495
3.0mm
sec
(PLC)
-
-
-
-
-
-
92
(6)
-
92
(6)
-
92
(6)
-
-
 
94
(6)
 
-
 
-
 
-
   - -
Water absorption
ISO 62
 
%
0.5
-
0.7
-
1.0
-
0.7
-
0.7
-
0.6
-
0.5
-
0.7
-
0.5
-
0.6
-
0.6
 - - -
Density
ISO 1183
 
g/cm3
1.05
-
1.06
-
1.09
-
1.14
-
1.23
-
1.30
-
1.28
-
1.31
-
1.38
-
1.45
-
1.46
 - 1.1 1.24
Volume Resistivity
Daicel Method
  
Ω･m
                                             102-105 100

NOTES
1. UL recognition File No. of Daicel Polymer is E47773.
2. Values with asterisk (*) are UL-recognized values.
3.CF-reinforced grades come under Item 5 (18) of Annex 1 of the Export Trade Control Order on the basis of the Foreign Exchange and Foreign Trade Law of Japan.

*"CELPURGE MA2" is recommendable for purging of Novalloy.
For purging of filled grades or carbonized contamination, "CELPURGE AW2 / high cleaning type" or "CELPURGE AG4 / super cleaning type" is especially recommendable.